退火对Fe66Cr8Cu1Nb3Si13B9条带磁弹性的影响测定了Fe66Cr8Cu1Nb3Si13B9合金带退火后纳米晶引起的变化来观察磁场与合金杨氏模量的关系。将3mm宽、25μm厚的Fe66Cr8Cu1Nb3Si13B9非晶合金带材切成5cm长...
Effect of Annealing on Magnetoelasticity of Fe66Cr8Cu1Nb3Si13B9 Strips The change of the nanocrystals in the Fe66Cr8Cu1Nb3Si13B9 alloy ribbon after annealing was measured to observe the relationship between the magnetic field and the Young’s modulus of the alloy. The 3mm wide, 25μm thick Fe66Cr8Cu1Nb3Si13B9 amorphous alloy strip cut into 5cm long ...