Stoichiometric Ni0.5Zn0.5Fe2O4 powders were produced by self-propagating high temperature synthesis (SHS). The effects of NiCO3 content in the raw materials on the microstructure and magnetic properties of Ni-Zn ferrite powders were systematically studied