The interface evolution of TiAl/Ti6242 joint produced by transient liquid phase(TLP) bonding with Ti,Cu foils as insert metals was investigated. The results sho
Samples of Ti26(Ti-V-Sn-Cr-Al-Zr-Nb) alloy were compressed on the Gleeble-1500 heat stimulation machine. The compression test was carried out at 900-1 150 ℃ an
Hot compressive deformation test of Ti-Al-Cu-Si alloy was performed on Gleeble-3500 hot-Simulator over the range of deformation temperature from 1 000 to 1 300
<正>2024 aluminum matrix composites reinforced with different size AlN particles (0.5, 4 and 10μm) were fabricated by the squeeze-casting technology. The aging