采用Gleeble3500热模拟试验机试验研究了直接车削用非调质钢SG4201(/%:0.42C,0.50Si,1.40Mn,0.009P,0.005S,0.02Nb,0.06V,0.015N)在1000~1250℃加热0~300s的奥氏体晶粒长大行为,并建立了该钢奥氏体晶粒长大模型。试验结果表明,加热时间30S时,奥氏体晶粒粗化温度和铌迅速大量固溶的温度为1100℃左右;奥氏体晶粒长大激活能约为110.8kJ;确立SG4201钢铸坯均热不宜超过1150℃。工业生产结果表明,当铸坯均热温度≤1150℃,终