论文部分内容阅读
通过对回收的废旧复合辊环材料进行重熔和离心铸造,制备了由耐磨WCP颗粒增强的复合层与Fe-C合金基体组成再生复合材料辊环,采用MMS-1G高速销-盘摩擦磨损试验机、扫描电镜(SEM),研究了100N、150N和200N载荷下滑动速度对再生复合辊环摩擦性能的影响。结果表明,不同载荷条件下,随滑动速度的增加,再生复合辊环的磨损率均出现幅度很小的波动现象,而摩擦系数先降低后缓慢增加。在相同滑动速度条件下,磨损率明显随载荷的增加而增大,而摩擦系数随载荷的增加而降低。再生复合辊环在低速条件下的磨损机理主要为犁沟磨损和塑性变形,而当滑动速度较高时,表现为粘着磨损、氧化磨损和磨粒磨损。
By remelting and centrifugal casting of waste recycled composite roll ring material, a roll of recycled composite material composed of wear-resistant WCP particle reinforced composite layer and Fe-C alloy matrix was prepared, and the friction and wear of MMS-1G high- The influence of the sliding speed on the tribological properties of the regenerated composite roll was studied under the load of 100N, 150N and 200N by SEM, SEM and SEM. The results show that under different loading conditions, with the increase of the sliding speed, the wear rate of the regenerated composite roll ring fluctuates with a small amplitude, while the friction coefficient decreases slowly and then increases slowly. At the same sliding speed, the wear rate obviously increases with the increase of load, while the friction coefficient decreases with the increase of load. The wear mechanism of the regenerated composite roll ring at low speed is mainly furrow and plastic deformation, while when the sliding speed is high, it shows adhesive wear, oxidized wear and abrasive wear.