The segregation and diffusion of boron during heat treatments were studied.The influence of boron contents, aging time and applied stress on FeMo2B2 formation was also studied.Finally, the effects of boron contents and FeMo2B2 formation on the high temperature strength were studied.Boron atoms were segregated to prior austenite grain boundary during normalizing treatment.And these boron atoms were slowly diffused into the grain interior during tempering and aging at 700 ℃.The FeMo2B2 phase was only formed after 1,000 h aging at 700 ℃ in alloy containing 196 ppm boron.The formation of FeMo2B2 phase is accelerated by the applied stress.It was expected that the formation of FeMo2B2 is closely related to the redistribution of boron atoms.The tensile strengths at 700 ℃ are increased with the increase of boron contents.However, the formation of FeMo2B2 phase results in lower tensile strength.