【摘 要】
:
The rich porous structure,high surface area and surface doping make nitrogen doping mesoporous carbon materials (N-MPC) attractive in various areas,including ad
【机 构】
:
College of Chemical and Pharmaceutical Engineering,Hebei University of Science and Technology,Shijia
论文部分内容阅读
The rich porous structure,high surface area and surface doping make nitrogen doping mesoporous carbon materials (N-MPC) attractive in various areas,including adsorption separation,electrochemical energy storage,catalysis and other fields.Herein,polyvinylpyrrolidone (PVP) is introduced into the polymeriza-tion process of assembly of phenol/formaldehyde (PF) resin by means of hydrogen bonds and electrostatic interaction,which not only leads to the formation of uniform mesopores,but also leads to the increase of specific surface area and nitrogen doping.The amount of PVP and annealing temperature has no obvious effect on morphology,but subsequently has effect on the specific surface area and pore volume.When appropriate PVP dosage and annealing temperature are adopted,the obtained N-MPC shows abundant mesoporous,high surface area and suitable nitrogen doping.As electrode materials in supercapacitor,the N-MPC shows good performance with high capacitance good stability and rate performance,presenting its excellent promising in energy storage.
其他文献
Radiation defects-induced plastic flow localization is the origin of loss of ductility in irradiated metals.Defect-free channels (DFCs) are a typical form of st
Composition dependence of martensitic transformations as well as the magnetic properties for the Ni2Mn1+xIn1-x (0.25 ≤ x ≤ 0.58) alloys were investigated by u
Thermoelectric (TE) materials and devices have attracted great attention due to their ability to con-vert waste heat to electrical power and active cooling.Howe
Understanding the densification behaviours and formation mechanisms of defects are essential to fabricate high quality and high strength aluminium components us
Based on the purpose of solving the “secondary absorption” of adjacent nanowires and the lateral emission in the GaN nanowire arrays (NWAs) cathode,an exponen
Microindentation creep tests on an electrodeposited extremely fine (4.9 nm) nanograined (ng) Ni-14.2 at.% Mo (Ni-14.2Mo) at both room temperature (RT) and liquid
Li2TiSiO5 receives much interest recently in lithium-ion battery anodes because of its attractive Li-insertion/extraction potential at 0.28 V (vs.Li+/Li),which
Density change is ubiquitous in phase transformation,and it can induce melt convection which strongly influences the crystal growth.Here,an anisotropic lattice
A novel 2D/2D BizMoO6/g-C3 N4 step-scheme (S-scheme) composite by loading Au as cocatalyst was suc-cessfully fabricated using a photoreduction and hydrothermal