Significant efforts have been made in revealing the mechanism of thaumasite formation in concrete, which continues to be fraught with ambiguities and dissension. Chemical method was employed to synthesize pure C3S, C2S, C3A, ettringite, and thaumasite, an
【机 构】
:
School of Environmental and Materials Engineering, Yantai University, Yantai 264005, China;School of
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
论文部分内容阅读
Significant efforts have been made in revealing the mechanism of thaumasite formation in concrete, which continues to be fraught with ambiguities and dissension. Chemical method was employed to synthesize pure C3S, C2S, C3A, ettringite, and thaumasite, and X-ray diffraction (XRD), Raman spectroscopy and infrared spectroscopy (IR) were used to identify thaumasite from other hydrates. To investigate the direct route of thaumasite formation, C3S, C2S, gypsum, and calcium carbonate were used to prepare a cement paste so that the interference of ettringite formation can be avoided. The indirect route of thaumasite formation was also studied by considering the effect of C3A or ettringite content on thaumasite formation. Results show that thau-masite can be definitely generated in the absence of aluminium-bearing minerals or ettringite under appropriate conditions, while the ettringite presence promotes the thaumasite formation. No evidences support the heteroge-neous nucleation route in this work. It is concluded that the method mentioned in this work can surely be used to investigate the mechanism of thaumasite formation, and thaumasite can form by both direct and woodfordite routes.
其他文献
Zinc oxide nanoparticles were synthesized using bovine serum albumin as stabilizers through a facile one-pot strategy in aqueous media. The morphology and crystal phase of the zinc oxide nanoparticles were determined by transmission electron microscopy, X
The surface reconstructing of vermicular alpha-alumina exposed under electron-beam irradiation was investigated by a scanning electron microscope with 0.5 keV beam energy and by a transmittance electron microscope at room temperature and 90 K, respectivel
Fly ash and diatomite were mixed uniformly and ground within various time scale and fly ash/diatomite admixtures with variable particle sizes were obtained. Effects of particle size distributions of the admixtures on the mechanical properties and porosity
We prepared graphene oxide(GO) saturable absorber (SA) successfully through optical deposition method, which is a simple but effective approach to deposit various materials onto substrate under the effects of light, and investigated several factors that i
Barium ferrite micro/nano fibers were successfully prepared via the electrostatic spinning by using dimethyl formamide (DMF) as the solvent, and poly vinyl pyrrolidone (PVP) as the spinning auxiliaries. Effects of strontium substitution on the structure,
Single crystalline calcium chloroborate (Ca2B5O9Cl) whiskers with uniform diameter have been fabricated by a two-step process. The precursor was firstly prepared by the sedimentation reaction between CaCl2, H3BO3 and NaOH aqueous solutions, and then sinte
The damage process and corrosion ion distribution in concrete, which was exposed to 60 and 170 drying-immersion cycles of sulfate solution, were systematically investigated. The effects of plain concrete, plain concrete mixed with 4 and 8 kg/m3 modified P
At the initial rolling temperature of 250 to 400 ℃,AZ31B magnesium alloy sheets were hot rolled by four different rolling routes.Microstructures and mechanical properties of the hot-rolled magnesium alloy sheets were analyzed by optical microscope and ten
This paper aimed to improve the water-retention performance and basic physical properties of sulfoaluminate cement (SAC)-based planting cementitious material.The effect of natural zeolite on the performance of SAC-based planting material was investigated.