【摘 要】
：
The effects of different Bi contents on the properties of Sn solders were studied. The interfacial reaction and growth behavior of intermetallic compounds (IMCs) layer (η-Cu6Sn5 + e-Cu3Sn) for various soldering time and the influence of Bi addition on the
【机 构】
：
Key Lab for Robot & Welding Automation of Jiangxi Province, Mechanical & Electrical Engineering Scho
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
The effects of different Bi contents on the properties of Sn solders were studied. The interfacial reaction and growth behavior of intermetallic compounds (IMCs) layer (η-Cu6Sn5 + e-Cu3Sn) for various soldering time and the influence of Bi addition on the thermal behavior of Sn-xBi solder alloys were investigated. The Cu6Sn5 IMC could be observed as long as the molten solder contacted with the Cu substrate. However, with the longer welding time such as 60 and 300 s, the Cu3Sn IMC was formed at the interface between Cu6Sn5 and Cu substrate. With the increase of soldering time, the thickness of total IMCs increased, meanwhile, the grain size of Cu6Sn5 also increased. An appropriate amount of Bi element was beneficial for the growth of total IMCs,but excessive Bi (≥ 5 wt％) inhibited the growth of Cu6Sn5 and Cu3Sn IMC in Sn-xBi/Cu microelectronic interconnects. Furthermore, with the Bi contents increasing (Sn-10Bi solder in this present investigation), some Bi particles accumulated at the interface between Cu6Sn5 layer and the solder.
其他文献
The hardfacing alloys with different concentrations of titanium were deposited on carbon steel substrates by shielded metal arc welding, and the effect of titanium content on the microstructure characteristics of the hardfacing alloys was investigated. Th
In order to improve microstructure distribution and mechanical properties of Mg alloy joint by annealing treatment, die-casting AZ31 Mg alloy was successfully welded at rotation speed of 1400 rpm and travel speed of 200 mm/min. The welded joints were anne
In order to explore the application of magnetron co-sputtering in fabricating the amorphous alloy, Zr-contained amorphous films were prepared by this technique and investigated by scanning electron microscope, energy disperse spectroscopy and X-ray diffra
Magnesium alloys with superhydrophobicity are constructed by controlling rough surface structure and grafting long hydrophobic alkyl chains. Changes of morphology, phase structure, chemical composition as well as wettability, corrosion resistance of super
The effect of Mo on the morphology,crystal structure and hydrogen sorption properties of Mg/C composites prepared by reactive milling was studied.Transmission electron microscopic (TEM) observation shows that Mg/C composites prepared with the addition of
Effect of ultrasonic vibration on deformation in micro-blanking was investigated with copper foils of different grain sizes using a developed device. It is found that maximum shearing strength is decreased by ultrasonic vibration, and this effect becomes
For TA15 titanium alloy, slip is the dominant plastic deformation mechanism because of relatively high Al content. In order to reveal the grain-scale stress field and geometrically necessary dislocation (GND) density distribution around the slip traces an