【摘 要】
：
Ultrasonic vibration-assisted ELID(UVA-ELID)grinding is utilized as a novel and highly efficient processing method for hard and brittle materials such as cerami
【机 构】
：
School of Electrical and Mechanical Engineering,Pingdingshan University,Pingdingshan 467000,China;Sc
论文部分内容阅读
Ultrasonic vibration-assisted ELID(UVA-ELID)grinding is utilized as a novel and highly efficient processing method for hard and brittle materials such as ceramics.In this study,the UVA-ELID grinding ZTA ceramics is employed to investigate the influence of thermomechan-ical loading on the characteristics of oxide film.Based on the fracture mechanics of material,the model of internal stress for oxide film damage is proposed.The thermomechanical loading is com-posed of mechanical force and the thermal stress generating from grinding temperature.The theo-retical model is established for the mechanical force,thermal stress and internal stress respectively.Then the finite element analysis method is used to simulate the theoretical model.The mechanical force and grinding temperature is measured during the actual grinding test.During the grinding process,the effect of grinding wheel speed and grinding depth on the thermomechanical force and the characteristics of oxide film is analyzed.Compared with the conventional ELID(C-ELID)grinding,the mechanical force decreased by 25.6％and 22.4％with the increase of grinding wheel speed and grinding depth respectively,and the grinding temperature declined by 10.7％and 12.8％during the UVA-ELID grinding.The thermal stress in the latter decreased by 16.3％and 20.8％respectively,and internal stress reduced by 12.3％and 15.6％.It was experimentally found that the topographies of oxide layer on the surface of the wheel and the machined surface in the latter was better than that in the former.The results indicate that the action of ultrasonic vibration establish a significant effect on the processing.Subsequently,it should be well considered for future reference when processing the ZTA ceramics.
其他文献
慢性肾功能不全在学术上被称作慢性肾功能衰竭(英文简称CRF),是一种临床上常见的慢性疾病。调查结果显示,全球有8.5亿慢性肾脏疾病患者,每年的死亡人数超过200万。我国肾脏疾病的发病率也呈现上升趋势,特别是慢性肾功能不全终末期患者,临床上也被称作尿毒症患者,主要表现症状为恶心呕吐、胸闷气短、尿少浮肿等,多发于中老年群体。因为其并发症较多且需长期住院治疗,费用较多,患者在财力、生理和心理上都饱受痛苦,这对护理人员而言是极大的挑战,不仅要对患者的身体进行精心地照顾,还需要及时对患者进行心理疏导。
In-situ ceramics particle reinforced aluminum matrix composites are favored in the aero-space industry due to excellent properties.However,the hard ceramic part
4 三维扫描激光雷达在接下来的篇幅中,将阐述如何使用三维激光雷达来进一步监测周围环境,并识别环境中的目标(如建筑物、树木以及道路等)。在该案例中,采用了西克公司生产的MRS 6000激光雷达(见图13)。图13 MRS 6000三维激光雷达MRS 6000激光雷达是一个多层扫描传感器,包含24个非接触激光束。其扫描频率为10 Hz, 可以实时生成周边环境的激光点云。一种独特的多边形镜面技术使得MR
目前双频带频率选择表面(Frequency Selective Surface,FSS)结构存在的通带选频性能有限。为了提高太赫兹频段通带滤波器件的性能,设计了一种基于频率选择表面的太赫兹双通带滤波器。该器件主要由三层正四边形的同心金属铜环组成,中间加载了介质衬底。金属层与衬底的厚度均为0.04λ,其中λ为低频波段的波长,单元尺寸为0.15λ。根据等效电路法分析了该结构产生双频通带的原因,并对设计的结构优化作了进一步的讨论。通过改变等效电路元件的参数等价地调整了原始结构的几何参数。仿真结果与理论计算基本吻
本文对用于飞行器极性测试的六自由度并联台进行了研究,分析了六自由度并联台技术背景及其在飞行器极性测试领域应用的可行性,给出了六自由度并联台总体设计方案,对平台关键指标进行了仿真验证,系统地阐述了六自由度并联台在飞行器极性测试应用过程中的关键技术和方法。
乳腺癌是全球女性发病率和死亡率最高的癌症。采用红外热成像技术能发现早期乳腺癌,并降低死亡率。借鉴了国内外的相关研究成果,采用冷环境及热电激发双重诱导下的红外热成像方法来解决小尺寸癌变组织和乳腺深部癌变组织的红外热成像应用效果差的问题。红外热成像的对比度显著增加了,且通电模式下的温度对比度提高了26.5%。研究表明,热对比度主要受癌变组织大小、深度和温度的影响,同时还受环境温度和换热系数的影响。通过同时控制环境和热源温度的措施提高了热对比度,预期乳腺癌的早期筛查效果可提高50%以上。
在中华五千年灿烂的诗文曲赋中,有种诗词没有诗经的风雅,没有唐诗、宋词、元曲的委婉,也没有当代诗歌的随意,但诗词的情怀却大义凛然,令人难忘。因为,诗词是蘸着信念和鲜血写就的。每次吟诵,这些诗句所蕴含的诗魂在眼前跳动。不,这不是诗,是一个个鲜活生命凝成的。
针对传统以经验为主的数控制造项目管理带来的资源冲突及工作滞后等问题,以某型号结构件数控制造项目管理为例,在制定初始进度计划和分析制造过程关键路径的基础上,采用关键链方法优化项目进度计划,并在实际生产中进行应用。结果表明,该方法能够避免资源浪费、进度拖延等现象,保证结构件交付节点,为飞机结构件数控制造项目进度安排探索了管理路径。
研究了InSb红外焦平面探测器的区域性过热盲元问题。通过故障分析以及有针对性的排查对比试验,排除了封装、胶水填充和划片等因素,并将故障定位在钝化工艺前。通过对钝化前的InSb材料片表面进行X射线光电子能谱测试,发现它含有Al和As等杂质元素,存在钝化前材料表面杂质含量较多的隐患。杂质元素在PN结的耗尽区形成杂质能级,加载电压后容易导致PN结漏电流较高,使I-V特性退化,从而形成过热盲元。通过缩短器具洗液的更换周期并且分隔使用多个生产线的器具,可以减少材料表面的杂质附着,使区域性过热盲元问题得到有效解决。