The thermal shock experiment of Au-Al bonding has been carried out.The mechanical characteristics,structure morphology and electrical characteristics degradatio
【机 构】
：
School of Physics Science and Technology,Central South University,Changsha 410083,China;National Key
论文部分内容阅读
The thermal shock experiment of Au-Al bonding has been carried out.The mechanical characteristics,structure morphology and electrical characteristics degradation mechanism have also been researched.No cracks were observed in the bonding interface,and the bonding ioints also showed good mechanical characteristics with pull stress of 3.0 to 12.0 g.Due to high temperature,the Au-Al intermetallic compound Au5Al2 with high resistibility was formed,which ultimately led to electrical failure.For the samples that were fabricated on the basis of the present technique,the bonding reliability has been evaluated.It has been found that the lifespan rule obeys the Weibull distribution,and at a high temperature of 150℃ under 95%confidence level,the estimated results are η=547 h,m=3.83.In a room temperature environment,the Au-Al bonding samples’ lifespan has also been predicted on the basis of the rule of reliability evaluation.The result shows that the lifespan is about 20 years,while the reliability degree is 90%.
其他文献
本组11例中男性8例、女性3例,起病的中位年龄70岁(45—86岁)。6例慢性淋巴细胞白血病(CLL)发生于多发性骨髓瘤(MM)之前2—3年,2例在诊断CLL时骨髓中浆细胞为1—2％,3例查了血
洋地黄糖甙类已沿用一百多年,迄今在治疗非梗阻性快速心率的低排性心力衰竭病人中仍不失为有效药物,但通过现代技术手段的检测及临床观察,对其长期正性收缩作用已引起怀疑,
In the present study,the effects of pH and initial Ca2+-H2PO4-(Ca-P) concentration on fibroin mineralization were studied.The crystal growth of calcium phosphat
A potassium titanate biological thin film/titanium alloy biological composite was fabricated by way of bionic chemistry.The biocompatibility fn vitro of Ti-15Mo
The structure of hair was replicated via a sol-gel process using human hair as a template.When using silicate and tetraethoxysilane(TEOS)as the precursor,the ce
A low-cost visual sensmg system is developed to realize weld seam tracking in gas metal arc welding(GMAW).The system consists of a commercial CCD camera,narrow-
尽快证实供者骨髓是否植入,具有实践和理论意义。染色体标记在骨髓移植后2—3用左右可证实植入。而红细胞酶或抗原通常要延迟至90天左右,这与受者红细胞延留和移植后的早期
一、考试要求《建筑材料》考试旨在测试考生对工程中常用建筑材料性质方面的基本知识的理解以及利用材料性质进行工程应用的能力。对各类建筑材料基本知识的要求由低到高分
High Mn is added in line pipe steels to strengthen them.Also,Mn lowers the phase transformation temperature,which is an advantage because it lowers the rolling
The shape-stabilized phase change materials (PCMs)composed of paraffin wax and silica were prepared in O/W emulsion with cetyl trimethylamine bromide as emulsif