<正>Not only the isothermal oxidation behaviors at 900-1 300℃for 20 h in air of bulk Ti3AlC2 with 2.8% TiC which was sintered by hot pressing with the additive
Using calcium hydroxide and sodium silicate as starting materials, two kinds of calcium silicate hydrates, CaO · SiO2 · H2O and 2CaO · SiO2 ·