A Ni-rich TiNi alloy was processed by Equal Channel Angular Extrusion (ECAE) at 500℃. After four passes ECAE treatment, microstructure of the alloy was refined but slightly inhomogeneous, to sub-micron scale, approximately 0.5~0.6 μm. Comparing with the s