The thermal stability of Al3(Sc,Zr) precipitates in the cold worked Al-Mg-Sc-Zr alloy after elevated temperature exposure was investigated. The evaluation was c
【机 构】
：
Institute of Metal Research
论文部分内容阅读
The thermal stability of Al3(Sc,Zr) precipitates in the cold worked Al-Mg-Sc-Zr alloy after elevated temperature exposure was investigated. The evaluation was conducted using room temperature tensile, Vickers hardness, optical metallography and scanning electron microscope (SEM) with the backscatter. The results show that the Al3(Sc,Zr) precipitates and mechanical properties have no obvious change, and the grains keep elongated along the working direction as that in cold worked sample after exposure at 300 ℃ for 1 000 h. The coarsening of Al3(Sc,Zr) precipitates occurs and is no longer effective on the recrystallization resistance, and partial recrystallization is observed after 400 ℃ exposure. In particular, after 500 ℃ exposure, the hardness decreases drastically and the alloy has fully recrystallized due to the obvious coarsening of Al3(Sc,Zr) precipitates.
其他文献
To find new chalcogenide glass possessing larger second-order non-linearity,glasses with compositions Ge-Ga-X-S (X=P,As,Sb) were prepared via melt quenching tec
Oxygen reduction(OR)on Teflon-bonded carbon electrodes with manganese oxide as catalyst in 6 mol/L KOH solution was investigated using AC impedance spectroscopy
Free-standing diamond films were prepared by hot filament chemical vapor deposition (HFCVD) method under different conditions. Inter-digital transducers (IDTs)
A new kind of amorphous active brazing alloy foil with the composition of Ti40Zr25Ni15Cu20 was successfully synthesized using melt spinning in roll forging mach
The bentonite was modified using Ca-bentonite as a matrix and octadecyl/ hexadecyl ammoniumsized by dispersing it into the dimethyl benzene-methyl alcohol syste
The rare earth manganite BaLn2Mn2O7 (Ln=rare earth element) has a Sr3Ti2O7-type layered perovskite structure with double-block oxygen octahedra belonging to the
The solution algorithm (SOLA) method was used to solve the velocity and pressure field of the thermal flow filling process, and the volume of fluid (VOF) method
A quasi 0-dB coupler composed of a composite right-/left-handed transmission line (CRLH TL) and a conventional right-handed transmission line (RH TL) is present
The titanium barium glass microspheres doped with Er2O3 were designed and prepared. The components of the glass sample were 25TiO2-27BaCO3-8Ba(NO3)2-5ZnO2-10CaC
Nanoparticles of red long afterglow phosphor Sr3Al2O6: Eu2+ were prepared by microwave irradiation method at a power of 680 W and a processing time of 15 min. T