【摘 要】
：
用硅溶胶铝矾土涂料和莫来石、煤矸石砂等,在密度为0.05~0.08g/cm~3的气化模上制备型壳,干燥后,在不同温度下进行型壳的失模试验.结果表明,在300~1000℃范围内失模时,型壳大
【机 构】
：
沈阳铸造研究所rrrrrrrrn,沈阳铸造研究所rrrrrrrrn,沈阳铸造研究所rrrrrrrrn,沈阳铸造研究所
论文部分内容阅读
用硅溶胶铝矾土涂料和莫来石、煤矸石砂等,在密度为0.05~0.08g/cm~3的气化模上制备型壳,干燥后,在不同温度下进行型壳的失模试验.结果表明,在300~1000℃范围内失模时,型壳大量开裂,在100~300℃范围内失模时,型壳不开裂.通过对气化模温度一尺寸特性及型壳失水收缩过程分析发现,高温下型壳的开裂是因其失水收缩严重受阻所致;最佳失模温度为160~200℃.
Silica sol bauxite coating and mullite, coal gangue sand and so on, the density of 0.05 ~ 0.08g / cm ~ 3 gasification mold prepared shell, after drying, at different temperatures under the shell of the mold The results show that when the mold is in the range of 300 ~ 1000 ℃, the mold shell will crack a lot and the mold will not crack when the mold is lost in the range of 100 ~ 300 ℃. Water shrinkage process analysis found that the cracking of high temperature shell is due to a serious blockage of water loss and contraction; the best loss of temperature is 160 ~ 200 ℃.
其他文献
实验采用微波辅助合成了1-乙基-3-甲基咪唑四氟硼酸([Emim]BF4)离子液体,采用多种方法表征了该离子液体的结构。构建了离子液体[Emim]BF4、水和乙醇的脱硫体系,并对脱硫工艺
以甲苯二异氰酸酯、聚醚二醇、二羟甲基丙酸为原料,通过高分子反应得到预聚体,将此预聚体在低浓度的氨基硅烷偶联剂溶液中扩链,制得一种氨基硅烷偶联剂改性的聚氨酯水乳液.性
随着大数据、云计算、人工智能、区块链等新一代信息技术领域的快速发展,全国各地各类数据中心的规模迅速扩张,无论是硬件配置的改善,还是软件性能的提升,都给互联网产业的发展带来巨大的变化,在深刻地影响着人们生活的同时,数据中心的发展也成为众多专家学者研究的热点。服务器是数据中心进行高效运转的关键,因此,保证服务器的稳定运行至关重要,相应地对服务器故障诊断技术的要求也越来越严格。传统的创新方法已难以实现对
零售终端建设在现代烟草营销中具有非常重要的作用,相对于传统零售终端而言,现代零售终端的功能更加丰富,对于提升零售户经营能力和盈利水平,保持行业健康持续发展具有更高价
为了提高薄层罩面的抗滑性能,基于多点支撑骨架状态的混合料体积设计方法(V-S),引进7.1mm的筛孔作为粗集料级配控制的筛孔尺寸。利用压碎筛分试验的方法重新确定了分界筛孔尺
目的通过体外细胞毒性试验，对碳纤维增强聚醚醚酮（CFR／PEEK）和钛合金两种材料的细胞毒性进行比较。方法培养人皮肤成纤维细胞（HSF）、人成骨细胞（HFOB）和鼠成纤维细胞（NIH3T3），提取两种材
软件产品是空间科学卫星工程的重要组成部分,其质量和可靠性直接关系任务的成败。根据我国空间科学卫星及其软件特点,空间科学先导专项总体确定了"体系为基、全面覆盖、分类
目的：探讨血压晨峰的危险因素，为采取针对性的预防或治疗措施提供依据。方法：研究对象于2011-01至2011-06在阜外心血管病医院进行24小时动态血压监测，并进行生化指标的检测，研究对
目的 通过分析喜庆元素在传播中华文化中的价值以及在网络使用中存在的问题,来阐述如何通过网络购物传播中华文化。方法 分析喜庆元素在网络购物宣传中的价值与存在的问题,来
目的研究Htr A1、MGP、BMP-2在人牙周膜细胞成骨分化中的生物学作用,初步探讨Htr A1与MGP、BMP-2在这一过程中的表达关系.方法首先用矿化诱导剂（β-磷酸甘油钠、地塞米松和抗