Effects of Polypropylene Fibers on the Physical and Mechanical Properties of Recycled Aggregate Conc

来源 :武汉理工大学学报(材料科学版)(英文版) | 被引量 : 0次 | 上传用户:lincl008
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
The viability of using polypropylene fibers (PPF) in concrete was largely studied. Yet, few of the existing research studies investigated the effects of PPF on the properties of concrete containing recycled concrete aggregate (RCA). Mixes with different RCA replacement ratios and different PPF content were designed and tested. The test results showed that the addition of PPF did not change significantly the compressive strength and the density of the concrete, but slightly decreased its modulus of elasticity and Poisson\'s ratio. The drop in the splitting tensile strength and the flexural strength due to RCA inclusions was to a large extent compensated by the PPF addition. The water absorption decreased and the percent voids increased with increased PPF addition. Correlations between the RCA content, the PPF content and the properties of concrete were studied. Useful regression models were proposed to predict the properties of concrete in relevant ranges of RCA and PPF content.
其他文献
The titanium carbide phase was synthesized in laser melted-pool in situ as the reinforced particles of nickel based composite coating on Ti-6Al-4V alloy surface using the nickel and graphite blending powder by laser cladding. The microstructure investigat
Ag-modified TiO2 nanoflowers were prepared using a two-step process. The experimental process is green and free from contamination and can be synthesized directly at room temperature. Compared with pure TiO2, Ag-modified TiO2 enhances the absorption of vi
We introduced a parameter rs (the radius of the pores where the meniscus forms), which is composed of two factors, i e, water loss and cumulative pore size distribution (PSD), to provide a better explanation of the influence of superplasticizers(SPs) on e
Si/Cu3Si@C composites encapsulated in CNTs network (SCC-CNTs) were synthesized via the combination of ball-milling and CVD methods. SCC-CNTs consist of conductive Cu3Si, amorphous carbon layer, cross-linked CNTs, and the etched pores, which can play the s
A simple route to synthesize the polyaniline (PANI) nanofibers with diameter about 150 nm was reported.In this strategy,the PANI nanofibers were fabricated by electrochemical deposition by using two-electrode configuration in 0.01 M aniline and 0.01 M H2S
A series of solar radiation tests for the polytetrafluoroethylene(PTFE) bulk and film samples were carried out using Q-SUN XE-3-HSC type Solar Radiation Simulator,with the test parameters as follows:radiation intensity is 1 120 W/m2,temperature is 55 ℃ an
A series of poly (ethylene oxide) (PEO) membranes with star-like structures for CO2/H2 separation were prepared by the photo-polymerization method.The structure of PEO membrane was characterized by Fourier transform infrared spectroscopy (FTIR).The therma
Nanocrystalline and amorphous LaMg12-type LaMg11Ni+xwt% Ni (x = 100, 200) alloys were synthesized by mechanical milling. Effects of Ni content and milling time on the gaseous and electrochemical hydrogen storage kinetics of as-milled alloys were investiga
Nitrogen doped multi-channel graphite was successfully prepared by using nitrogen doping and KOH etching technologies. The three-electrode and EIS tests indicates that the etched graphite possesses lower electrochemical resistance than the pristine graphi