A.Talaat等人采用Taylor-Ulitovsky工艺制造粒径为20~30nm的体心立方α-FeCo非晶先驱物,退火后粒径从23nm减小到11nm。制备态和涂玻璃层的退火态Fe_(38.5)Co_(38.5)B_(18)Mo_4Cu_1呈现矩形磁滞回线和
A. Taylor et al. Used the Taylor-Ulitovsky process to fabricate a body-centered cubic α-FeCo amorphous precursor with a particle size of 20-30 nm, and the particle size decreased from 23 nm to 11 nm after annealing. The annealed Fe_ (38.5) Co_ (38.5) B_ (18) Mo_4Cu_1 in the as-prepared and glass-coated layers show a rectangular hysteresis loop and