【摘 要】
:
The controlled preparation of hexagonal tung-sten trioxide(h-WO3)nanostructures was achieved by adjusting the pH of the precursor solution.The effect of the pH
【机 构】
:
College of Materials Science and Engineering,Key Laboratory of Advanced Functional Materials,Educati
论文部分内容阅读
The controlled preparation of hexagonal tung-sten trioxide(h-WO3)nanostructures was achieved by adjusting the pH of the precursor solution.The effect of the pH on the morphology,elemental composition,and pho-tocatalytic performance of the samples was characterized via X-ray diffraction(XRD),scanning electron micro-scopy,energy dispersive X-ray spectroscopy,and Raman spectroscopy.Ultraviolet-visible(UV-Vis)spectra were used to evaluate the absorbance and the photocatalytic performance of methylene blue.Photoluminescence(PL),electrochemical impedance spectroscopy,photocurrent response and Brunauer-Emmett-Teller(BET)were used to study the optical properties,electrical performance,and specific surface area of the WO3-nanostructures,respec-tively.The results indicate that the WO3 nanorods prepared at pH=1.0 exhibit the highest photocatalytic performance(87.4% in 1 h),whereas the WO3 nanoblocks prepared at pH=3.0 show the lowest.The photocatalytic performance of the one dimensional(1D)-nanorods can be attributed to their high specific surface area and charge transfer ability.The h-WO3 nanostructures were synthesized via a simple method and without a capping agent.They show an excellent photocatalytic performance,which is promising for their application in environment purification.
其他文献
Hot corrosion behavior in sulfate salt at 950 ℃of Rene N5 single-crystal superalloys with 3 wt% rhenium(NSR) was investigated compared with that of nickel-based
The main reason for the high strength in near-β titanium alloys is the ultrafine precipitation of the acicular secondary α phase in the β matrix.The purpose
NdCoO3 nanocrystals formed via glycine-nitrate combustion method followed by heat treatment has been systematically studied.Formation of NdCoO3 nanocrystals wit
For better performances of Ni-based catalysts at low temperatures,Ni/SiC catalyst doped with a little amount of additive La was successfully prepared.The catalytic CO methanation activity tests showed that 3%La-Ni/SiC catalyst was excellent at a low react
Recent studies suggested that the interactions between particles can induce aggregative nucleation and growth processes beyond those predicted by the traditional LaMer model of nanoparticle formation,but their nucleation and growth processes are still unc
In this work,CuFe2O4 hollow microspheres assembled with nanosheets(CuFe2O4 HMANs)were synthesized using a solvothermal method followed by an annealing treatment.The effects of annealing temperature on microstructure,chemical composition and gas sensing ch
Microstructures and tensile properties of a newβhigh-strength titanium alloy Ti-5321(Ti-5 Al-3 Mo-3 V-2 Zr-2 Cr-1 Nb-1 Fe)were investigated in this study.Four microstructures,including equiaxed microstructure(EM),bimodal microstructure(BM),basket-weave mi
A short process of Inconel 625 alloy tube was developed to solve the problems of the traditional extrusion process,and particular attention was paid on the hot deformation behavior of the as-cast Inconel 625 alloy.The hot compression experiments were perf
It is important to understand the correlation between grain morphology and intervariant boundaries of theαphase after heat treatment belowβtransus of the electron beam melted(EBMed)Ti-6 Al-4 V alloy.Scanning electron microscopy(SEM)and electron backscatte