Neodymium was incorporated into the three-dimensional mesoporous siliceous material TUD-1.In order to understand the chemical and morphological structure of the prepared material,several character-ization techniques were performed.The characterization results show the formation of highly distributed isolated Nd3+ions incorporated in the silica matrix in tetrahedrally coordinated structure,moreover no aggregation of separate phase(s)was/were observed.The prepared material was investigated as an adsorbent for methyl green(MG)dye in aqueous solution as a model cationic dye.The results show higher adsorption capacity for Nd-TUD-1 by almost 24 times higher than the neat parent TUD-1 material and more than 100 times higher than bulky Nd2O3 under neutral pH.The adsorption results were fitted perfectly with pseudo-second-order model.Moreover,the adsorption isotherms were perfectly fitted with Freundlich isotherm model which indicates the formation of a multilayer of the dye molecules onto the Nd-TUD-1 surface as a physisorption with endothermic nature.