It was found that typical Nbss /Nb5Si3 eutectic lamellar structure formed in the Nb-Mo-Si alloy. The interface between Nbss and Nb5Si3 phases was so strong that the alloy fractured mainly in the cleavage mode. In this paper, the fourth element was added w