The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C3H6, C3H6-N2 and C3 H6-H2 was
By using the experimental approach of dropping liquid, the coupling of three anionic wetting agents with ten dust samples of sulfide ores was studied, and parti