The sapphire (Al2O3) single crystal is a kind of excellent infrared transmission window materials. A large-sized sapphire (Φ225 mm×205 mm, 27.5 kg) was grown by SAPMAC method (sapphire growth technique with micro-pulling and shoulder-expanding at cooled center). Several kinds of inclusion in the large sapphire crystal were investigated by means of an optical microscopy (OM), scan-ning electron microscopy (SEM) and electron probe microanalysis (EPMA). The experimental results show that most inclusions are consisted of solid metallic and non-metallic particles as well as gas pores caused by the impurity of alumina as the raw material, the thermal dissociation of aluminum oxide melt and the reaction of the melt to the crucible material (Mo) at high temperatures. It is also found that in different crystal regions the inclusions are of varied sizes, morphology and chemical compositions. Finally, the measures to reduce and eliminate the inclusions are proposed to improve the crystal quality. A large-sized sapphire (Φ 225 mm × 205 mm, 27.5 kg) was grown by SAPMAC method (sapphire growth technique with micro-pulling and shoulder-expanding at Several kinds of inclusion in the large sapphire crystal were investigated by means of an optical microscopy (OM), scan-ning electron microscopy (SEM) and electron probe microanalysis (EPMA). The experimental results show that most inclusions are consisted of solid metallic and non-metallic particles as well as gas pores caused by the impurity of alumina as the raw material, the thermal dissociation of aluminum oxide melt and the reaction of the melt to the crucible material (Mo) at high temperatures. It is also found that in different crystal regions the inclusions are of varied sizes, morphology and chemical compositions. Finally, the measures to reduce and eliminate the inclusions are proposed to improve the crystal qualit y