This work was financially supported by the Major Pro- gram of National Natural Science Foundation of China (Nos 51090383 and 51090382) and the Scholarship Award for Excellent Doctoral Student granted
Mn2V2O7 thin films were deposited onto amorphous glass substrates using a chemical bath deposition method and different deposition time. X-ray diffraction(XRD)
To better understand the fracture behavior of TA15 titanium alloy during hot forming, three groups of experiments were conducted to investigate the influence of