【摘 要】
：
利用金相显微镜、扫描电镜和图像分析仪等检测手段,研究了离心渗铸铁基陶瓷颗粒复合材料的结合界面。结果表明:粒子在基体中分布均匀,粒子含有率可达23％—32％;粒子与基体界面无
【机 构】
：
东北工学院材料科学与工程系,东北工学院材料科学与工程系,东北工学院材料科学与工程系,东北工学院材料科学与工程系
论文部分内容阅读
利用金相显微镜、扫描电镜和图像分析仪等检测手段,研究了离心渗铸铁基陶瓷颗粒复合材料的结合界面。结果表明:粒子在基体中分布均匀,粒子含有率可达23％—32％;粒子与基体界面无元素富集,无反应产物,但加热至 900℃,保留 180 min后,SiC 开始有少量分解,Si 向基体方向扩散,C 在粒子周围富集;复合材料比基体材料耐磨性提高 40倍。
The bonding interface of centrifugal cast iron-based ceramic particle composites was studied by means of metallographic microscope, scanning electron microscope and image analyzer. The results show that the particles are uniformly distributed in the matrix and the content of particles is up to 23% -32%. There is no element enrichment and no reaction products at the interface between the particles and the matrix. However, when SiC is heated to 900 ℃ for 180 min, , Si diffuses to the matrix direction and C is enriched around the particles; the wear resistance of the composite material is 40 times higher than that of the matrix material.
其他文献
继Danchokn轨道用的减震系统的成功开发应用之后,对用石渣铺设的轨道中所用弹性枕木的发展要求是能够减少维修、减少振动和噪音。本文主要论述了减震铁路,即用弹性材料覆盖
金融风暴、经济危机,导致许多企业经营发生了严重困难,甚至开始走向破产,最直接的结果就是劳动者失业。 1986年《企业破产法(试行)》实施起来困难重重,新《企业破产法》十年
用复合铸造法制备的SiC_μ/Al复合材料,加热到一定温度并保温不同时间以改变其界面反应程度,通过确定复合材料中的分含量及其与温度和时间之间的相互关系,对界面反应动力学进
利用Co源强γ射线辐照制备金属超微粒子,并首次采用γ射线辐照—水热结晶联合法获得了Cu,Au和Cu—Au合金超细粉末,还初步讨论了超细粉的成核过程和考察了它们的形貌、晶粒大
本文简要地叙述拉压不同模量弹性理论,介绍该理论在弹性力学和复合材料力学领域中所取得的一些成果及其在工程中的应用。
This paper briefly describes the different modu
20世纪70年代以来,由于CCD器件的出现,人们开始研究使用相似技术的红外焦平面阵列(IRFPA)技术。80年代,该技术有了比较快的发展,但当时比较成熟、规模较大和均匀性较好的凝视
借助于SHPB和SHTB实验技术,在环境温度-50℃～+200℃和应变率低于3×10~3s~(-1)条件下,对穿甲弹用弹托材料LC_(4cs)铝合金的动态力学行为进行了实验测试分析,给出了材料在不同
研究了高性能热塑性树脂双酚 A 型聚砜(PSF)、酚酞型聚醚酮(PEK-C)增韧聚苯硫醚(PPS)的破坏韧性和破坏形态。实验表明:PSF 与 PEK-C 两种材料的加入都能改善 PPS 的冲击强度
为了模拟研究CONFORM连续挤压过程中金属的变形行为,本文设计了一种专门的模拟实验装置,并利用莫尔云纹法研究了模拟实验时金属塑性变形的分布情况。研究结果表明,CONFORM连
研究了人造花岗岩复合材料组成配方、性能测试及其应用。研制了MJ7116人造花岗岩磨床床身,并与铸铁床身进行了动态性能对比。
The composition formula, performance test a