【摘 要】
:
A nano-laminated Y3Si2C2 ceramic material was successfully synthesized via an in situ reaction between YH2 and SiC using spark plasma sintering technology.A MAX
【机 构】
:
Faculty of Materials Science and Engineering,Kunming University of Science and Technology,Kunming 65
论文部分内容阅读
A nano-laminated Y3Si2C2 ceramic material was successfully synthesized via an in situ reaction between YH2 and SiC using spark plasma sintering technology.A MAX phase-like ternary layered structure of Y3Si2C2 was observed at the atomic-scale by high resolution transmission electron microscopy.The lattice parameters calculated from both X-ray diffraction and selected area electron diffraction patterns are in good agreement with the reported theoretical results.The nano-laminated fracture of kink boundaries,delamination,and slipping were observed at the tip of the Vickers indents.The elastic modulus and Vickers hardness of Y3Si2C2 ceramics (with 5.5 wt% Y2O3) sintered at 1500 ℃ were 156 and 6.4 GPa,respectively.The corresponding values of thermal and electrical conductivity were 13.7 W·m-1 ·K-1 and 6.3× 105 S·m-1,respectively.
其他文献
介绍185/60R1482H TAXIPLUS出租车专用轮胎的设计。结构设计:外直径574 mm,断面宽195 mm,行驶面宽度138 mm,行驶面弧度高6.1 mm,胎圈着合直径350.1 mm,胎圈着合宽度153 mm,断面水平轴位置(H1/H2)0.9843,胎面采用3条花纹沟槽设计,花纹深度8.4 mm,花纹饱和度68.46%,花纹周节数60。施工设计:胎面采用三复合设计,胎侧采用双复合设计,1#和2#带束层使用3×0.30HT钢丝帘线,冠带层采用锦纶66帘线,胎体采用高模量低收缩聚酯帘线,采用一
研究硫化胶中炭黑燃烧特性与对应炭黑原材料特性的关系,利用两者间的关系分析不同硫化胶中的炭黑品种,评价炭黑分散性。结果表明:硫化胶中炭黑燃烧特征温度与对应炭黑的压缩吸油值和氮吸附表面积均呈显著线性关系,相关因数分别为0.8069和0.9541;根据炭黑燃烧特征温度及线性回归方程推导出硫化胶中炭黑的压缩吸油值和氮吸附表面积,可以判定硫化胶中的炭黑品种;硫化胶中炭黑燃烧特征温度低,在一定程度上可以表明炭黑分散性良好。
Chemical vapor deposition is an important method for the preparation of boron carbide.Knowledge of the correlation between the phase composition of the deposit and the deposition conditions (temperature,inlet gas composition,total pressure,reactor configu
通过生物质醇解制备液体燃料与化学品获得广泛关注,但该方法存在产物复杂、选择性低、反应机理不清等问题。本文主要研究具有不同聚合度的糖类在乙醇溶剂中的反应特性。结果表明:随着温度的升高,葡萄糖、蔗糖、纤维二糖的转化率提高,转化率大小均为葡萄糖>蔗糖>纤维二糖>纤维素;在160~200℃,葡萄糖主要生成5-羟甲基糠醛,纤维二糖主要产物由左旋葡萄糖变为5-羟甲基糠醛,而蔗糖主要产物由乙基-α-D-吡喃葡萄糖苷变为5-羟甲基糠醛。
天然气水合物储层的渗透率是影响水合物开采时气、水运移的关键,也是水合物开采潜力评价、资源评价、开采工艺选择等需要了解的关键参数。目前,国内外学者对天然气水合物储层的渗透率迚行了一定的研究并有了初步认识。但是,对于围压、轴向压力、水合物饱和度、赋存模式等对水合物沉积物渗透率的影响机制和机理还不清楚。本文在自主设计的水合物储层三轴渗透率测试平台上,实验研究了粒径、围压、轴向压力、水合物饱和度等对沉积物渗透率的影响。结果表明,采用不同围压测得的水合物沉积物渗透率存在较大差异:多孔介质粒径的减小会降低沉积物渗透率
K[J]768煤矿微震监测系统是实时监测煤矿微震事件的计算机在线测量系统.系统将计算机监测技术、数据通讯技术和传感器技术融为一体,实现了复杂环境条件下对煤矿井下的微震事
Gadolinium zirconate (GZ) is a promising candidate for next-generation thermal barrier coating (TBC) materials.Its corrosion resistance against calcium-magnesium-alumino-silicate(CMAS) needs to be further increased for enhancing its in-service life.As the
日本横滨橡胶株式会社(以下简称横滨橡胶)宣称,其参与的一项研究计划已突破性地开发出生物质高效生产丁二烯的技术.丁二烯是轮胎用合成橡胶的核心组分.工业丁二烯是石油热解
锑基硫属化合物是一类性质稳定、环境友好、元素含量丰富、带隙连续可调、光电性质优异的半导体材料,包括硒化锑(Sb2Se_3)、硫化锑(Sb2S_3)以及硒硫化锑[Sb2(S,Se)_3]等。其中,Sb2(S,Se)_3的带隙和太阳光谱的匹配度较高,比较适合作为太阳电池的光吸收层材料。以Sb2(S,Se)3为光吸收层的太阳电池取得了10%的认证能量转换效率,显示了锑基硫属化合物太阳电池的巨大潜力。本文
应急救援的能源保障与当地环境和应用场景密切相关,新能源技术的就地取材、高敁转化和原位供能等特点将为应急科技装备和相关人员的能源保障提供新的选择。本文以典型应用场景为技术案例,结合华南地区的新能源资源条件和应急救援场景的能源需求,分别对近岸岛屿、南海海洋、偏进山区和无人飞行器等场景迚行分析,探讨新能源技术在应急保障领域的解决方案和应用潜力,以期为新能源应急科技装备的収展提供借鉴。