Experiments were conducted to determine theresidual stresses with X-ray diffraction in the ma-trix of a SiC/Al composite after different thermaltreatments,and t
The isothermal section of the Fe-Cu-Niternary system at 1173 K was determined bymicroprobe analysis and diffusion triple technique.The experimental results show