最近,薄带连铸法很引人注目。特别是不锈钢与普通钢相比,由于生产量少和氧化皮生成量少,较适合于用薄带连铸法生产。日新制钢所和日立制作所着眼于薄带成形性优良的双辊法,为探索这种方法作为工业生产方法的可能性,首先用试验设备进行了SUS304不锈钢的铸造试验,研究了制得的薄带的特性。把120公斤经高频感应熔炼的SUS304不锈钢钢液通过中间包,在备有直径400mm、
Recently, the strip casting method is very attractive. Especially stainless steel compared with ordinary steel, due to less production and less scale oxide, more suitable for the production of thin strip casting. In order to explore the possibility of this method as an industrial production method, Nisshin Steel Works and Hitachi Manufacturing Co., Ltd. focused on a twin-roll method excellent in strip formability. First, a cast test of SUS304 stainless steel was carried out using a test apparatus. Thin band characteristics. The 120 kg of high-frequency induction melting stainless steel SUS304 through the tundish, with a diameter of 400mm,