【摘 要】
：
以Ti粉、C粉、TiN粉和Ni60A粉末为原料,利用氩弧熔覆技术在16Mn钢基材表面成功制备出Ni基增强相复合涂层,应用OM、SEM、XRD对复合涂层的显微组织和物相进行了分析。结果表明,
【机 构】
：
黑龙江科技大学材料科学与工程学院,鞍山钢铁有限公司,
论文部分内容阅读
以Ti粉、C粉、TiN粉和Ni60A粉末为原料,利用氩弧熔覆技术在16Mn钢基材表面成功制备出Ni基增强相复合涂层,应用OM、SEM、XRD对复合涂层的显微组织和物相进行了分析。结果表明,复合涂层物相由TiC、TiN颗粒,γ-Ni奥氏体枝晶和枝晶间的Cr23C6共晶组织组成。涂层的硬度(HV0.2)达到900,较基体16Mn钢提高了3倍多;相对耐磨性较基体16Mn钢提高了8倍。
Using Ti powder, C powder, TiN powder and Ni60A powder as raw materials, the Ni-based reinforced composite coatings were successfully prepared on the surface of 16Mn steel by argon arc cladding. The effects of OM, SEM and XRD Microstructure and phase were analyzed. The results show that the composite coating phase consists of TiC, TiN particles, γ-Ni austenite dendrites and Cr23C6 eutectic between dendrites. The hardness of the coating (HV0.2) reached 900, which was more than three times that of the matrix 16Mn steel. The wear resistance of the coating increased by 8 times compared with that of the matrix 16Mn steel.
其他文献
人们已经普遍认识到自由基与恶性肿瘤发生之间存在着一定的关系,机体内对自由基的清除有一完整的抗氧化防御系统,谷胱甘肽转移酶μ(GSTμ)在此系统中占有重要位置.本实验采用
目的 制备表达人c-jun氨基末端激酶(JNK)复制缺陷型重组腺病毒.方法 将重组穿梭载体pAdTrack-CMV-WT-JNK线性化后,与pAdEasy-1共转化大肠杆菌BJ5138,进行同源重组得到重组腺病毒载体.将重组腺病毒载体转染入包装细胞HEK293内制备复制缺陷型重组腺病毒,并经PCR及DNA测序鉴定.结果 JNK重组腺病毒载体能有效转染HEK293细胞并在细胞内成功包装,5 d后可以
汽车节温器是汽车发动机的关键部件,气密性要求高。通过对汽车节温器进行数值模拟分析,确定采用真空压铸工艺以减少产品的气孔缺陷。结合压实销技术对凝固的补缩过程施加控制
去年秋季在青岛市场上每公斤卖到了50元的冬枣,今秋竟“一落千丈”,最低价才卖6元钱。 今秋沾化冬枣在青岛市场上初市批发价每公斤在16元左右,零售价在20元左右,而去年同期
目的:探讨肿瘤患者实施心理干预的方法及其效果.方法:随机选取2002-08/2008-12期间我院收治的1862例肿瘤患者中120例,分为实验组(心理干预组)和对照组(传统教育组).结果:两组
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
以AT72镁合金为研究对象，设计了压铸工艺。通过密度测定、力学性能测试，研究了压铸工艺对AT72镁合金力学性能的影响。所讨论的压铸工艺包括：常规压铸、真空压铸、普通钢质冲头、
介绍了某化工设备上使用的钛合金叶轮铸件石墨型铸造工艺。分析了铸件产生气孔和叶片位置偏移等缺陷的原因。通过增加加工余量、提高离心转速和优化石墨型工艺,即加工余量由
以Cu-Al为基添加适量的Ni、Fe等在金属型模具中铸造一种多元铝青铜合金,利用失重法、扫描电镜、能谱仪(EDS)、X射线衍射仪等研究了固溶时效处理对该多元铝青铜合金腐蚀行为的
为了进一步优化猴头菇（Hericium erinaceus）工厂化栽培的培养条件,筛选优良菌种,本试验选择18种不同来源的猴头菇菌种作为试验材料,通过对各菌种的菌丝生长情况、菌丝生长速率