An M-type hexagonal ferrite BaTiCoFe10O19 was prepared by solid phase reaction by a partial 2Fe3+→Ti4++Co2+ substitution. The morphology observation and phase
The dependence of electrical properties of Ba0.92Ca0.08TiO3 PTC ceramics on the SiO2 or TiO2 content was studied. The dependence of room temperature resistivity