【摘要】 蒸汽管道是大型石化、钢厂等十分常见的一类管道，由于蒸汽管道的操作条件严苛，大多处于高温高压的环境中，一旦出现安全隐患问题就很容易导致危险事故发生。因此，企业的管理人员应重视压力管道的日常维护和定期检验工作，压力管道的检验人员更应当认真做好压力管道的定期检验，在检验中发现问题应及时告知企业，并提出合理可行的处理分析。本文将从蒸汽管道的定期检验必要性、管道的球墨化缺陷处理两个方面进行相关论述，以供参考。
【关键词】 15CrMo蒸汽管道;球墨化;缺陷处理;分析
【DOI编码】 10.3969/j.issn.1674-4977.2021.04.024
Analysis of Nodular Graphite of 15CrMo Steam Pipeline
WANG Zhen-yi
（Fushun Special Equipment Supervision and Inspection Institute，Fushun 113006，China）
Abstract： Steam pipelines are a very common type of pipelines in large petrochemicals and steel plants. Due to the harsh operating conditions of steam pipelines，most of them are in high temperature and high pressure environments. Once potential safety hazards occur，dangerous accidents can easily occur. Therefore，the management personnel of the enterprise should pay attention to the daily maintenance and regular inspection of the pressure pipeline，and the inspectors of the pressure pipeline should carefully conduct the regular inspection of the pressure pipeline. If problems are found during the inspection，they should promptly inform the company and propose reasonable and feasible treatments. analysis. This article will discuss the necessity of regular inspection of steam pipelines and the treatment of spheroidization defects of pipelines for reference.
Key words： 15CrMo steam pipeline;nodular graphite;defect treatment;analysis
蒸汽管道在石油化工企业中较为常见，可以说是石油化工企业生产运输必備的装置设备，而石化产品自身就具有高温高压、有毒有害、易燃易爆的特点，只有加强对承压设备的安全监管才能够保障其应用的稳定性，实现安全生产。承压设备监管体系的完善还能够进一步保障压力管道的安全运行，最终提高石油化工企业的经济效益。
1 发现问题
某石化热电厂蒸汽管道在运行4年后到达了下一个检验周期，压力管道的操作条件如下。
管道材质为：15CrMoG电站弯管，弯管规格426×16，R=1700 a=100;
操作压力：4.0 MPa;
操作温度：435 ℃;
介质：蒸汽。
检验员在对该弯管进行了定期检验，检验过程中通过测量硬度发现该弯管的硬度值超标，检测硬度HB117。由于硬度超标，检验员根据该管线的操作条件和材质对该弯管进行了进一步的金相组织检测，检测部位示意图见图1。
经检测发现15CrMoG电站弯管，原标准金相组织形态为铁素体+珠光体或贝氏体，实测金相组织未见珠光体或贝氏体形态，且硬度低于标准值HB130，硬度区间为（HB125-HB170）。根据金相组织检测结论判定该弯管的金相组织异常（见图2、图3），硬度低于标准值，球墨化5级。
2 问题处理
由于该弯管紧邻阀门和电动机附近，且高温高压的恶劣工况，球墨化5级，材质劣化严重，不能安全使用到下一个检验周期，因此检验员给出更换该弯管的处理意见。
3 问题分析
15CrMo系珠光体组织耐热钢，在高温下有较高的热强性和抗氧化性在510 ℃下高温使用，适合该管线的操作条件。但由于该弯管紧邻阀门和电动机附近，易发生冲刷减薄，同时根据车间工作日志发现时有超温超压的工况发生。因此造成了该管线的问题产生。
4 结语
综上所述，本次压力管道的定期检验工作中，合理地选择压力管道弯管的检测位置，选择在电动机、阀门的出口易发生冲刷减薄的部位。在硬度值异常后准确的给出了金相组织检测的要求，最终发现了该弯头存在的球墨化5级，材质劣化严重的缺陷，并及时准确的提出处理意见，为企业的安全运行提供了有利的保障。
【参考文献】
[1] 火电厂用15CrMo钢珠光体球化评级标准：DL/T 787-2001[S].
[2] 高压锅炉用无缝钢管：GB/T 5310-2017[S].
[3] 姜波.电站锅炉主蒸汽管道常用材料对比研究[J].科技创新与应用，2019（23）：78-79.
[4] 陈露贵，王志武，肖学柱.娘子关发电厂4号机组1号10CrMo910主蒸汽管组织性能评定[J].热力发电，2004（4）：60-62.
【作者简介】
王臻意（1973-），女，高级工程师，学士，研究方向为压力容器、压力管道现场安装监督检验。
【关键词】 15CrMo蒸汽管道;球墨化;缺陷处理;分析
【DOI编码】 10.3969/j.issn.1674-4977.2021.04.024
Analysis of Nodular Graphite of 15CrMo Steam Pipeline
WANG Zhen-yi
（Fushun Special Equipment Supervision and Inspection Institute，Fushun 113006，China）
Abstract： Steam pipelines are a very common type of pipelines in large petrochemicals and steel plants. Due to the harsh operating conditions of steam pipelines，most of them are in high temperature and high pressure environments. Once potential safety hazards occur，dangerous accidents can easily occur. Therefore，the management personnel of the enterprise should pay attention to the daily maintenance and regular inspection of the pressure pipeline，and the inspectors of the pressure pipeline should carefully conduct the regular inspection of the pressure pipeline. If problems are found during the inspection，they should promptly inform the company and propose reasonable and feasible treatments. analysis. This article will discuss the necessity of regular inspection of steam pipelines and the treatment of spheroidization defects of pipelines for reference.
Key words： 15CrMo steam pipeline;nodular graphite;defect treatment;analysis
蒸汽管道在石油化工企业中较为常见，可以说是石油化工企业生产运输必備的装置设备，而石化产品自身就具有高温高压、有毒有害、易燃易爆的特点，只有加强对承压设备的安全监管才能够保障其应用的稳定性，实现安全生产。承压设备监管体系的完善还能够进一步保障压力管道的安全运行，最终提高石油化工企业的经济效益。
1 发现问题
某石化热电厂蒸汽管道在运行4年后到达了下一个检验周期，压力管道的操作条件如下。
管道材质为：15CrMoG电站弯管，弯管规格426×16，R=1700 a=100;
操作压力：4.0 MPa;
操作温度：435 ℃;
介质：蒸汽。
检验员在对该弯管进行了定期检验，检验过程中通过测量硬度发现该弯管的硬度值超标，检测硬度HB117。由于硬度超标，检验员根据该管线的操作条件和材质对该弯管进行了进一步的金相组织检测，检测部位示意图见图1。
经检测发现15CrMoG电站弯管，原标准金相组织形态为铁素体+珠光体或贝氏体，实测金相组织未见珠光体或贝氏体形态，且硬度低于标准值HB130，硬度区间为（HB125-HB170）。根据金相组织检测结论判定该弯管的金相组织异常（见图2、图3），硬度低于标准值，球墨化5级。
2 问题处理
由于该弯管紧邻阀门和电动机附近，且高温高压的恶劣工况，球墨化5级，材质劣化严重，不能安全使用到下一个检验周期，因此检验员给出更换该弯管的处理意见。
3 问题分析
15CrMo系珠光体组织耐热钢，在高温下有较高的热强性和抗氧化性在510 ℃下高温使用，适合该管线的操作条件。但由于该弯管紧邻阀门和电动机附近，易发生冲刷减薄，同时根据车间工作日志发现时有超温超压的工况发生。因此造成了该管线的问题产生。
4 结语
综上所述，本次压力管道的定期检验工作中，合理地选择压力管道弯管的检测位置，选择在电动机、阀门的出口易发生冲刷减薄的部位。在硬度值异常后准确的给出了金相组织检测的要求，最终发现了该弯头存在的球墨化5级，材质劣化严重的缺陷，并及时准确的提出处理意见，为企业的安全运行提供了有利的保障。
【参考文献】
[1] 火电厂用15CrMo钢珠光体球化评级标准：DL/T 787-2001[S].
[2] 高压锅炉用无缝钢管：GB/T 5310-2017[S].
[3] 姜波.电站锅炉主蒸汽管道常用材料对比研究[J].科技创新与应用，2019（23）：78-79.
[4] 陈露贵，王志武，肖学柱.娘子关发电厂4号机组1号10CrMo910主蒸汽管组织性能评定[J].热力发电，2004（4）：60-62.
【作者简介】
王臻意（1973-），女，高级工程师，学士，研究方向为压力容器、压力管道现场安装监督检验。