【摘 要】
：
This work aimed to research the structure models of amorphous materials. Five amorphous and paracrystalline samples (natural or artiifcial) were investigated via29Si/27Al nuclear magnetic resonance (NMR) and field emission scanning electron microscopy/ene
【机 构】
：
School of Civil Engineering, Dalian University of Technology, Dalian 116024, China
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
This work aimed to research the structure models of amorphous materials. Five amorphous and paracrystalline samples (natural or artiifcial) were investigated via29Si/27Al nuclear magnetic resonance (NMR) and field emission scanning electron microscopy/energy dispersive spectroscopy (FE-SEM/EDS). The results of NMR showed the resonances of different specimens:-93.2 ppm,-101.8 ppm,-111.8 ppm for natural pozzolana opal shale (POS). These peaks were assigned to the Q2(2OH), Q3(OH)/Q4(1Al) and Q4 respectively. The results of27Al MAS NMR indicated that Al substituted for Si site in tetrahedral existing in the POS, while the Al/Si atomic ratio in opal was low (around 0.04). For the alkali-silicate-hydrate gel, there were at least three resolved signals assigned to Q0 and Q1, respectively. For the fused silica glass powder, there were the primary signals centered about at the range from-107 to-137 ppm, which were assigned to Q4 units. In addition, the peaks at around-98 and-108 ppm were corresponding to Q3(1OH) and Q4 units existing in aerogel silica structure.
其他文献
Layered double hydroxides (LDHs)/styrene-butadiene-styrene (SBS) copolymer modified bitumen was prepared by melt blending. The effect of LDHs on the ultraviolet (UV) aging behavior of SBS modifi ed bitumen was investigated. The changes of chemical structu
Overcasting is a new kind of dissimilar joining technique used to produce the aluminum(solid)/magnesium(liquid) bonding bi-metallic material in this study. For the Al/Mg (A390/AM60) bi-metallic samples, the interface microstructures are the research point
The effect of thermal shock, in an accelerated-corrosion environment spectrum, on the fatigue and corrosion behavior of 7B04-T6 aluminum alloy, was determined. The environment spectrum consists of two modules, namely: salt-spray corrosion and thermal shoc
Pouring temperature and time are the most important influencing factors on interfacial reaction during the centrifugal casting. When cast at high temperatures, the crucible becomes brittle and prone to cracking, and shows a low stability. In this paper, w
Low average temperature, large temperature difference and continual freeze-thaw (F-T) cycles have signiifcant impacts on mechanical property of asphalt pavement. F-T cycles test was applied to illustrate the mixtures’ compressive characteristics. Exponent
The microstructure and dynamic rheological characteristics of asphalt containing different polymer modifiers (crumb rubber, styrene-butadiene-styrene and crumb rubber mix with styrene-butadiene-styrene) at mid and high service temperature levels were inve