介绍了使用50 Hz/250 Hz双频淬火机床对一种锥形辊淬火的工艺。因淬火过程中感应器和辊子的间隙不断变化导致磁通效率也不断变化,故施加功率随辊子行程近似线性调整,使整个辊
论文部分内容阅读
介绍了使用50 Hz/250 Hz双频淬火机床对一种锥形辊淬火的工艺。因淬火过程中感应器和辊子的间隙不断变化导致磁通效率也不断变化,故施加功率随辊子行程近似线性调整,使整个辊身达到一致的淬火温度。辊子经检测和使用,淬火硬度及淬硬层深度均符合技术要求,表明双频淬火技术能够实现锥形辊的淬火。
The process of quenching a conical roll using a 50 Hz / 250 Hz dual frequency quench machine is presented. Due to the constant gap between the inductor and the roller during quenching, flux efficiency is also constantly changing. Therefore, the applied power is adjusted approximately linearly with the stroke of the roller to achieve a uniform quenching temperature throughout the barrel. The roller has been tested and used, quenching hardness and hardened layer depth are in line with technical requirements, indicating dual-frequency quenching technology to achieve tapered roller quenching.
其他文献
本项目在恶性疟疫苗候选分子裂殖子表面蛋白-2(MSA2)及环子孢子蛋白(CSP)的分子生物学特征和免疫原性研究的基础上,构建了CSP、MSA2之DNA疫苗,同时率先在国内外构建CSP、MSA2
对GCr15钢球阀经不同液氮保温时间和不同升温速度的深冷处理后的组织和力学性能进行了研究。结果表明:深冷处理可促使残留奥氏体转变为马氏体,细化组织并析出微细碳化物,提高
198 5年 5月至 1998年 12月我科对 5 6例直肠癌病人施行Dixon手术 ,取得了良好的效果。现报道如下。1 资料与方法本组 5 6例 ,男 3 8例 ,女 18例。年龄 2 2 72岁。肿瘤下缘
目的 了解社区居民成人体质指数(BMI)与血液中总胆固醇(TC)之间的关系.方法 随机整群抽样,对沈阳市社区＞50岁的2 274例居民进行身高、体重和TC等指标测定,并进行统计分析.结果
目的 分析辽宁省2011 2015年报告的狂犬病病例特征,为狂犬病防制工作提供科学依据.方法 对2011-2015年通过中国疾病预防控制信息系统报告的狂犬病病例的流行病学调查信息进行
研究了连续退火温度对550 MPa级热镀锌低合金钢组织性能的影响。结果表明,550 MPa级热镀锌低合金钢经连续退火后基体为铁素体加少量渗碳体,同时在铁素体中含有大量Nb、Ti碳氮
从材料特性、齿轮与花键两部位不同的渗碳层深度、渗碳和淬火前后允许的尺寸畸变量等方面,分析了18Cr2Ni4WA钢从动齿轮轴的热处理技术条件,提出了控制产品质量的相应措施。结
服役于高含硫油气勘测、开采的设备,受到介质、温度、压力的影响,容易发生应力腐蚀和应力腐蚀断裂(SSC和SCC),这就对金属材料的力学及耐腐蚀性能提出了苛刻的要求。本文对铁
采用扫描电子显微镜(SEM)自带的INCA250能谱仪对DD6单晶合金真空热处理过程中真空度、真空充气压力、加热温度、保温时间对其表面氧化作用的影响规律进行了研究。结果表明,在
1995年1月至2002年12月,我科对手术治疗的40例70岁以下男性直肠癌病人,按年龄、手术方式分组比较术后性功能变化.