【摘 要】
：
研究了不同固溶处理工艺对CN617耐热合金组织和硬度的影响。结果表明,CN617合金在1125~1200℃温度范围内固溶处理时,晶粒正常长大,平均晶粒尺寸从31μm增长到206μm;超过1175
论文部分内容阅读
研究了不同固溶处理工艺对CN617耐热合金组织和硬度的影响。结果表明,CN617合金在1125~1200℃温度范围内固溶处理时,晶粒正常长大,平均晶粒尺寸从31μm增长到206μm;超过1175℃固溶时,富铬和钼碳化物基本回溶。在1175℃固溶保温不同时间后,平均晶粒尺寸与硬度很好地符合Hall-Petch关系式。
The effect of different solution treatment on the microstructure and hardness of CN617 heat-resistant alloy was studied. The results show that the grains grow normally and the average grain size increases from 31μm to 206μm when the CN617 alloy is solution treated in the temperature range of 1125-1200 ℃. When the solid solution temperature exceeds 1175 ℃, the chromium and molybdenum carbide are basically dissolved . After 1175 ℃ solution heat preservation for different time, the average grain size and hardness fit well with the Hall-Petch relation.
其他文献
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
Using sea ice concentration dataset covering the period of 1968-2002 obtained from the Hadley Center of UK, this paper investigates characters of Antarctic sea
医用镁合金的降解特性直接影响其在心血管支架和骨替换材料等领域的应用。本研究在保持与生理体液氯离子浓度一致的基础上,选用镁合金AZ31B分别浸入NaCl溶液,KCl溶液,MgCl2溶
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
本文通过分析呼和车站运用车保有量的主要影响因素,从车站作业组织优化,设备能力提升,人员素质提高,管理制度与考核措施等方面探讨了如何减少车站运用车保有量,以进一步提高
本文针对地球天然脉冲电磁场(ENPEMF)信号的非平稳性特点,通过采用归一化STFT-WVD变换(NSTFT-WVD)提取芦山MS7.0地震前地表天然脉冲电磁场信号的时频特性,来研究大地震发生前
以6013型铝合金为试验对象,研究了反复镦压工艺制备细晶材料,消除合金各向异性的可行性。采用金相显微镜,透射电镜研究了6013型铝合金反复镦压对合金组织和性能的影响。结果
采用基于密度泛函理论(DFT)的平面波超软赝势方法,结合广义梯度近似(GGA),计算了Ce原子在α-Fe晶内、晶界和自由表面的杂质形成能,在此基础上,研究了稀土元素Ce在α-Fe中的占
针对铁基牺牲阳极在工业生产中的应用,分析了铁基牺牲阳极对电位较正金属(如Cu、不锈钢和钛合金)阴极保护的可行性。综述了几种铁基材料作为牺牲阳极的性能,以及作为牺牲阳极
针对化学微蚀刻法和微细电镀法制备微流控芯片金属模具进行了工艺对比研究。采用激光共聚焦显微镜分别检测表征由这两种加工工艺制备所得的模具微结构特征,对其侧壁陡度、尺