Current practice in analysis and design of blast doors subjected to blast loading considers only simple boundary conditions and material properties. The boundar
The structural and dielectric properties of Ba0.92Sr0.08Ti0.95Sn0.05O3(BSTS)+x(molar ratio, %)Y3+ ceram-ics are investigated. Combining the lattice parameters a