【摘 要】
：
The magnetic refrigeration(MR)utilizing magnetocaloric effect(MCE)has been recognized as an envi-ronmentally friendly and energy efficiency technology.Here we presented the magnetic properties and MCE in Pr-doped La1-xPrxFe12B6(x=0.05-0.2)itinerant-electr
【机 构】
：
Key Laboratory of Electromagnetic Processing of Materials(Ministry of Education),Northeastern Univer
论文部分内容阅读
The magnetic refrigeration(MR)utilizing magnetocaloric effect(MCE)has been recognized as an envi-ronmentally friendly and energy efficiency technology.Here we presented the magnetic properties and MCE in Pr-doped La1-xPrxFe12B6(x=0.05-0.2)itinerant-electron metamagnetic(IEM)compounds.A small amount of Pr doping La site can greatly improve the peak values in the magnetic entropy change ΔSM(T)curves,especially under relatively low magnetic field changes(ΔH).Additionally,the peak temperature increases gradually and the magnetic hysteresis reduces gradually with increasing x.The observed MCE in present La1-xPrxFe12B6 compounds is related to its field-induced first-ordered IEM transition.The peak values of ΔSM for La1-xPrxFe12B6 compounds reach 13.4,15.4,12.5 and 13.0 J/(kg K)at Tc～58,68,72 and 89 K for x=0.05,0.10,0.15 and 0.2 under ΔH of 0-7 T,respectively.The corresponding relative cool-ing power values are 462.3,480.7,372.4 and 375.7 J/kg.The present La1-xPrxFe12B6 compounds could be good candidates for active MR application if the magnetic and thermal hysteresis can be further reduced.The present work indicates that the LaFe12B6-based material system could also exhibit promising magne-tocaloric performances.
其他文献
Microstructural and mechanical behavior of heat treatable Al-4.6Cu binary alloy reinforced with graphene nanoplates(GNPs)in different heat treatment status were investigated in this paper.The addition of GNPs significantly enhanced the yield strength and
基于搅拌摩擦的固相增材制造是大型轻质合金构件成形制造的新技术,已成为国内外先进成形制造领域研究的热点之一.本文对目前国内外基于搅拌摩擦的金属固相增材制造技术及其相关工艺机理的研究现状进行了分析和总结.常见的基于搅拌摩擦的固相增材制造技术可分为三类:基于搅拌摩擦搭接焊原理,使板材逐层堆积,从而获得增材构件的搅拌摩擦增材制造(friction stir additive manufacturing,FSAM)技术;采用中空搅拌头,通过添加剂(粉末或丝材)进行固相搅拌摩擦沉积的增材制造(additive fri
Perovskite solar cells(PSCs)have become a promising alternative to sustainable energy due to their high power conversion efficiency(PCE)and low-cost processing.However,the practical applications of PSCs are still limited by the trade-off between high perf
In K4750 alloy,the evolution of grain boundary(GB)precipitates,including the degradation of blocky MC carbide particles and the precipitation of granular/needle-like η phase particles,were observed after long-term aging(LA)at 750℃for 8000 h.During MC degr
The degradation of acid orange Ⅱ(AO Ⅱ)by a nanoporous Fe-Si-B(NP-FeSiB)electrode under the pulsed square-wave potential has been investigated in this research.Defect-enriched NP-FeSiB electrode was fab-ricated through dealloying of annealed Fe76Si9B15 amo
In the present investigation,the growth kinetics of interfacial reaction layer products between cubic boron nitride(CBN)and Cu-Sn-Ti filler metal has been thoroughly investigated.Detailed morphological and compositional features of respective compounds ha
Acoustic emission(AE)of 316L stainless steel with of low Ni content shows,under tension,simultane-ously three avalanche processes.One avalanche process relates to the movement of dislocations,the oth-ers to martensitic transformations and detwinning/twinn
Magnetic liquid metal droplets(MLMDs)have been proven to be very important in many fields such as flexible electronics and soft robotics.Usually,soft magnetic particles such as nickel(Ni)and iron(Fe)are mixed or suspended into the liquid metal to obtain s
A series of silicates with double shell hollow sphere morphology were prepared by hydrothermal method with ultra-high temperature calcined,and used in the field of electromagnetic(EM)wave absorption.By characterizing the chemical composition,crystal struc
The creep inconsistency between dendrite core and interdendritic region is investigated in a nickel-based single crystal superalloy under 1373 K and 137 MPa.Two specimens with higher and lower degree of el-emental inhomogeneity on dendritic structures are