上海有色金属研究所与上海有色金属压延厂共同研制的“高强度变形铍青铜研究”课题鉴定会于1982年9月21日至23日在上海市召开。17个单位共47名代表参加了会议。会议听取了研制单位的课题研究总结与工艺报告,以及五家应用单位与复验单位的试验和复验报告。与会代表经过充分的讨论一致认为: 1.添加微量镁显著地抑制了高强度变形铍青铜的晶界不连续析出、扩大了时效温
Shanghai Institute of Nonferrous Metals and Shanghai Nonferrous Metal Calendering Plant jointly developed the “high-intensity deformation of beryllium bronze” project identification will be September 21, 1982 to 23 held in Shanghai. A total of 47 representatives from 17 units attended the meeting. Meeting heard the research unit developed the project summary and process reports, as well as five application units and reinspection unit test and reinspection report. Participants after full discussion agreed that: 1. Addition of trace magnesium significantly inhibited the high-strength deformation of the beryllium bronze discontinuity precipitation, expanding the temperature aging