【摘 要】
：
Al-20Sn-1 Cu powders were prepared by gas atomization in an argon atmosphere with atomizing pressures of 1.1 and 1.6 MPa.The characteristics of the powders are
【机 构】
：
National Engineering and Technological Research Center for Non-ferrous Metals Composites
【基金项目】
：
国家重点基础研究发展计划(973计划)
论文部分内容阅读
Al-20Sn-1 Cu powders were prepared by gas atomization in an argon atmosphere with atomizing pressures of 1.1 and 1.6 MPa.The characteristics of the powders are determined by means of dry sieving,scanning electron microscopy (SEM),optical microscopy (OM),and X-ray diffractometry (XRD).The results show that the powders exhibit a bimodal size distribution and a higher gas pressure results in a broad size distribution.All particles in both cases are spherical or nearly spherical and satellites form on the surface of coarse particles.Dendritic and cellular structures coexist in the particle.With decreasing particle diameter,the secondary dendrite arm spacing (SDAS) decreases and the cooling rate increases.The particles processed under high gas atomization pressure (1.6 MPa) exhibit a lower SDAS value and a higher cooling rate than those of the same size under low gas atomization pressure (1.1 MPa).The XRD results show that the Sn content increases with decreasing particle size.
其他文献
分析了增加新对象后,决策表的决策属性关于条件属性的条件熵变化原理.并在此基础上提出了一种新的增量核求解算法.该算法只需找到与新对象属性值相等的条件类和决策类就可以
The singularly perturbed bifurcation subsystem is described,and the test conditions of subsystem persistence are deduced.By use of fast and slow reduced subsyst
A novel method was designed to solve reinforcement learning problems with artificial potential field. Firstly a reinforcement learning problem was transferred t
A modified solid-state route was attempted to prepare Y0.95 Eu0.05PO4 PDP phosphor,involving milling a powdered mixture of YCl3,EuCl3,and (NH4)2HPO4 and calcini
Polyaniline(PAn) doped with multiple sulfonic acid system of dodecylbenzenesulfonic acid(DBSA) and sulfosalicylic acid(SSA) was synthesized by emulsion polymeri
The silicon assistant method to increase the reaction yield of carbothermal reduction of silica at a lower temperature is reported. The effect of silicon on the
The variations of intrinsic coercivity and remanence of sintered Nd-Fe-B magnets with ultra-high intrinsic coercivity were investigated.The results showed that
The effects of various factors on the flow speed of interdendritic melt were analyzed in detail in the process of continuous casting slabs. When the solid-liqui
The space time spreading,superimposed training sequences,and space-time coding are used to present a multiple input and multiple output(MIMO)systems model,and a
To improve the durability as well as to reduce the cost of anodes, the IrO2+MnO2 composite coating anodes for NaC10 production were prepared by thermal decompos