Chromium nitride(Cr2N) thin films were prepared by a DC magnetron sputtering technique. The deposition temperature was raised from 50 to 300°C, and its influence on the film structure and refractive index was investigated. X-ray diffraction analysis shows that the crystalline structure of the films transforms from the(101) to(002) oriented hexagonal Cr2 N phase as the increase of substrate temperature above 50°C, and a highly textured film grows at 100°C. An empirical relation between the crystalline orientation and infrared active modes of the films is obtained, i.e., the Fourier transform infrared(FTIR) spectrum of the film prepared at 50°C exhibits only A1(TO) mode. The prominent peak in the FTIR spectra of the film prepared above 50°C is assigned to the E1(TO) mode and is correlated with the(002) or c-axis oriented hexagonal wurtzite phase of Cr2 N. In the surface analysis of atomic force microscopy, a transformation from the featureless surface to columnar-type morphology is observed with the increase of substrate temperature from 50 to 100°C, exhibiting c-axis oriented crystallite growth. A further increase in substrate temperature to 200°C causes the c-axis crystallites to merge, resulting in the formation of voids. The refractive index(n) of the deposited films is obtained using spectroscopic ellipsometry.
Chromium nitride (Cr2N) thin films were prepared by a DC magnetron sputtering technique. The deposition temperature was raised from 50 to 300 ° C, and its influence on the film structure and refractive index was investigated. X-ray diffraction analysis shows that the crystalline Structure of the films transforms from the (002) oriented hexagonal Cr2 N phase as the increase of substrate temperature above 50 ° C, and a highly textured film grows at 100 ° C. An empirical relation between the crystalline orientation and infrared active modes of the films is obtained, ie, the Fourier transform infrared (FTIR) spectrum of the film prepared at 50 ° C exhibits only A1 (TO) mode. The prominent peak in the FTIR spectra of the film prepared above 50 ° C is assigned to the E1 (TO) mode and is correlated with the (002) or c-axis oriented hexagonal wurtzite phase of Cr2 N. In the surface analysis of atomic force microscopy, a transformation from the featureless surface to columnar-type morphology is observed with the increase of substrate temperature from 50 to 100 ° C, exhibiting c-axis oriented crystallite growth. A further increase in substrate temperature to 200 ° C causes the c-axis crystallites to merge, resulting in the formation of voids. index (n) of the deposited films is obtained using spectroscopic ellipsometry.