【摘 要】
:
The oxidation behavior of NiAl-30.75Cr-3Mo-0.25Ho alloy from 1300 to 1500 K in air atmosphere was investigated. The results reveal that oxidation resistance of
【机 构】
:
School of Electromechanism Engineering,Institute of Metal Research
论文部分内容阅读
The oxidation behavior of NiAl-30.75Cr-3Mo-0.25Ho alloy from 1300 to 1500 K in air atmosphere was investigated. The results reveal that oxidation resistance of the alloy is improved by the addition of Ho. At 1500 K, the oxidation kinetic curve obeys the parabolic law (n≈0.5), whereas the oxidation kinetic curve of the tested alloy follows the cubic relations (n≈0.3~0.4) from 1300 to 1450 K. An activation energy of about 261 kJ·mol-1 was determined for the tested alloy. It is found that a continuous and compact Al2O3 layer has formed on the surface of NiAl-30.75Cr-3Mo-0.25Ho alloy after oxidation 100 h at various tested temperatures. A rich-Ho solution formed on the boundaries of Cr(Mo) phase. Doped little amount of Ho in NiAl-31Cr-3Mo alloy promotes the transformation from θ-Al2O3 phase to α-Al2O3 phase, and decreases the size of Al2O3 and the crack forming in the oxidation scale prolongs the spalling time of the film at high temperature. The volatilizing oxides of Cr, Mo and the reactive element effects (REEs) make the mass gain lower than that of pure NiAl.
其他文献
Rare earth and far-infrared mineral composite materials were added to ceramic glazes to prepare easy-cleaning ceramic. The morphology of easy-cleaning ceramic w
A new process for electrolytic production of a perfluorinated compound, (CF3)3N, using lanthanum nickel oxide-coated Ni sheet anode in the (CH3)4NF·4.0HF melt
The post-growth treatment of a [100]-oriented diamond film was performed to improve the film quality. The characteristic of post-growth film was investigated by
Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x=0, 8, 15, 20) with the diameter of Φ 2~6 mm were manufactured by electric arc smelting, h
LiNi0.85Co0.15-xAlxO2 samples (x=0.025, 0.05 and 0.10) were prepared by solid state reaction at 725℃ doped by Co-Al has been tried to improve the cathode perfo
The effects of thermal annealing on oxygen behavior and carrier lifetimes of mc-Si wafers were investigated by means of FTIR and QSSPCD during single step and t
Sapphire single crystals are widely used in many areas because of the special physic properties and important application value. As an important substrate mater
The feasibility of using metal optics or negative ε materials, with the aim of reducing the transversal extent of waveguided photonic fields to values much les
We propose an on-demand multipath routing algorithm in a mobile ad hoc network for video transmission and evaluate its real world performance in video streaming
The influence of coarse Cu-bearing particles, matrix and subgrain boundary precipitates on the stress corrosion susceptibility of the Al-Zn-Mg-Cu alloys was inv