With processes of arc melting, inductive melting and copper mold suction casting, a plate Fe-based bulk amorphous alloy Fe60Co8Zr10Mo5W2B15 with a thickness of 1mm was prepared. The surfaces and fractures of the cast bulk amorphous alloy were agleam and with typical metallic luster. The glass transition temperature(Tg), supercooled liquid region(△Tx)and reduced glass transition temperature(T rg)of the prepared Fe-based amorphous alloy are 884 K,63 K, and 0.611 respectively. The fracture toughness of the cast bulk amorphous alloy is at the level of 1.6 MPa·m1/2.