Micron sized hexagon- and flower-like nanostructures of lead oxide(α-PbO_2) have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by the simple variation of applied voltage from 2-6 V between the electrodes. Lead sheet was used as an anode and platinum sheet served as a cathode. Anodic oxidation at 2 V resulted in the variable edge sized(1-2 μm) hexagon-like structures in the electrolyte. When the applied potential was increased to 4 V a structure of distorted hexagons consisting of some flower-like structures were obtained. Further increment of potential up to 6 V resulted in flower like structures of α-PbO_2 having six petals. The diameter of the flower-like structures was ~200-500 nm and the size of a petal was ~100-200 nm.
Micron sized hexagon- and flower-like nanostructures of lead oxide (α-PbO_2) have been synthesized by very simple and cost effective routes of anodic oxidation of lead sheet. These structures were easily obtained by the simple variation of applied voltage from 2-6 Anodic oxidation at 2 V resulted in the variable edge sized (1-2 μm) hexagon-like structures in the electrolyte. When the applied potential was increased to 4 V a structure of distorted hexagons consisting of some flower-like structures were obtained. Further increment of potential up to 6 V resulted in flower like structures of α-PbO_2 having six petals. The diameter of the flower-like structures was ~ 200-500 nm and the size of a petal was ~ 100-200 nm.