论文部分内容阅读
5甚长波红外探测器这项研制工作的目标是,通过制造截止波长为16μm、工作温度为55 K的红外焦平面阵列提高人们对甚长波红外波段的认识水平。试验中,研究人员将1个特制的MCT探测层混成在Sofradir公司生产的CL176型标准硅读出集成电路(320×256元、像元间距为30μm、电荷处理能力大于36 Me-)上。其中,探测层主要分为三部分:(1)CdZnTe衬底(在0.8μm至红外波段是
5 Very Long Wave Infrared Detector The goal of this development was to raise the level of awareness of the very long wave infrared band by fabricating an infrared focal plane array with a cutoff wavelength of 16 μm and an operating temperature of 55 K. In the test, the researchers mixed a specially fabricated MCT probe layer with a CL176 standard silicon readout integrated circuit (320 × 256 cells, pixel spacing of 30 μm and charge handling capacity of greater than 36 Me-) manufactured by Sofradir. Among them, the detection layer is mainly divided into three parts: (1) CdZnTe substrate (in the 0.8μm to infrared band is