Fine TiFe series alloy powder was fabricated by magnesothermic reduction of ilmenite as main raw material. Adiabatic temperature of the FeTiO3-Mg system was studied through thermodynamic analysis. Meanwhile, the characteristics of TiFe series alloy were described by XRD, SEM and grading analysis. It is shown that combustion synthesis of the FeTiO3-Mg system can carry out due to its strong exothermic reaction through adiabatic temperature calculate. Ultrafine TiFe series alloy powder after leached for 5 h has reasonable phases and morphology with the particle distribution of 0.2 to 1 μm. It indicates that in-situ magnesothermic reduction of natural ilmenite is a feasible way to fabricate ultrafine powder with a relatively lower cost.
Fine TiFe series alloy powder was fabricated by magnesothermic reduction of ilmenite as main raw material. Adiabatic temperature of the FeTiO3-Mg system was studied through thermodynamic analysis. Meanwhile, the characteristics of TiFe series alloy were described by XRD, SEM and grading analysis. It is shown that combustion synthesis of the FeTiO3-Mg system can carry out due to its strong exothermic reaction through adiabatic temperature calculate. Ultrafine TiFe series alloy powder after leached for 5 h has reasonable phases and morphology with the particle distribution of 0.2 to 1 μm. It indicates that in-situ magnesothermic reduction of natural ilmenite is a feasible way to fabricate ultrafine powder with a relatively lower cost.