In this study, fatigue properties and fracture mechanism of dissimilar Al–Mg–Si/Al–Zn–Mg aluminum alloys friction stir welding(FSW) joints were investigated and the effect of the sheet configuration on the fatigue behavior of the FSW joints was also discussed. Results showed that the joints owned better fatigue properties when the Al–Zn–Mg aluminum alloy was placed at the advancing side(AS). At 10~7 cycles, the fatigue strengths of Al–Zn–Mg–AS and Al–Mg–Si–AS joints were, respectively, 105.6 and 90.1 MPa. All joints fractured at the heat-affected zone at the Al–Mg–Si alloy side. Transmission electron microscopy results showed that better fatigue property of the Al–Zn–Mg–AS joint was associated with the bridging effect of the bigger secondary phase particles.
In this study, the fatigue properties and fracture mechanism of dissimilar Al-Mg-Si / Al-Zn-Mg aluminum alloys friction stir welding (FSW) joints were investigated and the effect of the sheet configuration on the fatigue behavior of the FSW joints was also The results showed that the joints owned better refractory properties when the Al-Zn-Mg aluminum alloy was placed at the advancing side (AS). At 10-7 cycles, the fatigue strengths of Al-Zn-Mg-AS and Al- All joints fractured at the heat-affected zone at the Al-Mg-Si alloy side. Transmission electron microscopy results showed that better fatigue property of the Al-Zn-Mg -AS joint was associated with the bridging effect of the bigger secondary phase particles.