Ni-matrix composite coating containing AI2O3 nano-particles is prepared by brush plating. The effects of the nano-particles on the microstructure, microhardness and tribological properties of the composite coating under the lubrication of a diesel oil containing sand are investigated. The results show that the microstructure of the composite coating is finer than that of the pure nickel coating due to the codeposition of the nano-particles. When the nano-particle concentration in the electroplating bath reaches 20 g/L, the microhardness, and wear resistance of the composite coating is as much as 1.6 times and 1.3-2.5 times of those of the pure nickel coating respectively. The main hardening mechanism of the composite coating is superfine crystal grain strengthening and dispersion strengthening. The composite coating is characterized by scuffing as it slides against Si3N4 under the present test conditions.
Ni-matrix composite coating containing AI2O3 nano-particles is prepared by brush plating. The effects of the nano-particles on the microstructure, microhardness and tribological properties of the composite coating under the lubrication of a diesel oil containing sand are investigated. The results show that the microstructure of the composite coating is finer than that of pure nickel coating due to the codeposition of the nano-particles. When the nano-particle concentration in the electroplating bath reaches 20 g / L, the microhardness, and wear resistance of the composite coating is as much as 1.6 times and 1.3-2.5 times of those of pure nickel coating respectively. The main hardening mechanism of the composite coating is superfine crystal grain strengthening and dispersion strengthening. The composite coating is characterized by scuffing as it slides against Si3N4 under the present test conditions.