The stripe cracks which formed along rolling direction on the surface of Ti–4Al–2V alloy cold-rolled sheet were observed by stereoscope, scanning electron microscope(SEM), and energy-dispersive spectrometer(EDS). Morphology analysis indicates that cracks are dominantly in zigzag shape, with 10–30 mm in length and less than 10 lm in depth, and there is no evidence of crack tips. Chemical composition analysis shows that crack regions feather high oxygen concentration while smooth surface is at normal oxygen level. It is obvious that the occurrence of strip cracks is mainly related to residual oxide on the surface of Ti–4Al–2V alloy cold-rolled sheet.
The stripe cracks which formed along rolling direction on the surface of Ti-4Al-2V alloy cold-rolled sheet were observed by stereoscope, scanning electron microscope (SEM), and energy-dispersive spectrometer (EDS). Morphology analysis that that cracks are dominantly in zigzag shape with 10-30 mm in length and less than 10 lm in depth, and there is no evidence of crack tips. Chemical composition analysis shows that the crack regions feather high oxygen concentration while smooth surface is at normal oxygen level. It is obvious that the occurrence of strip cracks is mainly related to residual oxide on the surface of Ti-4Al-2V alloy cold-rolled sheet.