论文部分内容阅读
Four alloys TMS-75 (Base), Base+B, Base+C and TMD-103 (Base+B+C) with varying levels of B, C were directionally solidified (DS), and their weldability was investigated by bead-onplate electron beam welding.It was found that cracking occurred in the weld-m