采用本体聚合法 ,进行接枝、交联 ,对国内大量生产的 0 10树脂进行改性。经过正交实验 ,优选出 3个条件作为合成目的产品的最佳条件。其产品的软化点、粘度、韧性等性能与 0 10树脂相比有了大幅度提高 ,并已达到国外进口同类产品指标 ,可作为热熔胶粘剂广泛用于彩电、汽车、热缩材料等领域。该合成路线原料立足国内 ,来源丰富 ,工艺简单易行 ,无环境污染 ,为 0 10类树脂的应用开辟了一条新途径 ,具有良好的经济效益和社会效益
Using bulk polymerization, grafting, crosslinking, mass production of 0 10 resin modification. After orthogonal experiment, three conditions were selected as the optimal conditions for the synthesis of the target product. Its softening point, viscosity, toughness and other properties compared with 0 10 resin has been greatly improved, and has reached the target of similar imported products abroad, can be used as a hot melt adhesive widely used in color TV, automotive, heat shrinkable materials and other fields. The synthetic route based on the domestic raw materials, rich in source, process is simple and easy, without environmental pollution, 0 10 for the application of resin has opened up a new way, with good economic and social benefits