The bonding of steel-mushy Al-7graphite was studied. The relationship between interfacial shear strength of bonding plate and solid fraction of Al-7graphite mushy was obtained, and the interfacial structure of bonding plate was determined. The results showed that: under the condition of 500℃ for preheat temperature of steel plate and 10mm/s for rolling speed, the largest interfacial shear strength of bonding plate was 70.1 MPa when solid fraction of Al-7graphite mushy was 34.6%.
The bonding of steel-mushy Al-7graphite was studied. The relationship between interfacial shear strength of bonding plate and solid fraction of Al-7graphite mushy was obtained, and the interfacial structure of bonding plate was determined. The results showed that: under the condition of 500 ° C for preheat temperature of steel plate and 10 mm / s for rolling speed, the largest interfacial shear strength of bonding plate was 70.1 MPa when solid fraction of Al-7graphite mushy was 34.6%.