针对Al2O3、SiO2物料在10型扁平式气流磨上利用正交实验方法确定了最优工况,在最优工况下,得出两种物料的极限粒径分别为4.8μm,3.2μm
For the Al2O3 and SiO2 materials, the optimum working conditions were determined by the orthogonal experimental method on a 10-type flat jet mill. Under the optimal conditions, the ultimate particle sizes of the two materials were found to be 4.8 μm and 3.2 μm, respectively